<div class="csl-entry">Philipp, H. (2013). <i>Korrosionsverhalten von Nickel-Aluminium-Bronzen in Süßwasser</i> [Diploma Thesis, Technische Universität Wien]. reposiTUm. https://doi.org/10.34726/hss.2013.16310</div>
</div>
-
dc.identifier.uri
https://doi.org/10.34726/hss.2013.16310
-
dc.identifier.uri
http://hdl.handle.net/20.500.12708/8144
-
dc.description
Abweichender Titel laut Übersetzung der Verfasserin/des Verfassers
-
dc.description
Zsfassung in engl. Sprache
-
dc.description.abstract
In der vorliegenden Arbeit sollte das Korrosionsverhalten von Nickel-Aluminium- Bronzen (NAB) in Süßwasser untersucht werden. Anstoß zu den Untersuchungen wurde durch einen Korrosionsfall an Laufrädern einer Gussbronze des Typs CuAl10Fe5Ni5-C in einem Wasserkraftwerk gegeben. Der Angriff äußerte sich in Form grüner Pusteln aus Malachit mit der Zusammensetzung Cu2CO3(OH)2.<br />NAB ist ein widerstandsfähiges Material und findet vor Allem in marinen Anwendungen weiten Einsatz. Trotz umfangreicher Literatur bezüglich seines Korrosionsverhaltens in Salzwasser werden seine Süßwasseranwendungen und damit verbundene Problemstellungen nicht diskutiert. Die Turbinen wurden in Form absenkbarer Module konstruiert, in denen die Laufräder mit dem umgebenden Laufradring aus nicht rostendem Stahl leitend kontaktiert waren.<br />Die angestellten Versuche korrelieren mit im Kraftwerk gewonnenen Daten und zeigen an, dass ein mikrobielles Ennoblement des Laufradringes aus nicht-rostendem Stahl zu einem Anstieg dessen Potentials führte. Diese Potentialerhöhung gegenüber der NAB war zur Ausbildung eines effektiven Kontaktelements (Bimetallkorrosion) ausreichend, in welchem die Auflösung der NAB-Turbinen in relevanten Zeiträumen (Wochen) vorangetrieben wurde.<br />
de
dc.description.abstract
In the present work the corrosion behaviour of nickel aluminium bronzes (NAB) in freshwater was investigated. Motivation was given due to the occurrence of corrosion on turbine runners made of cast nickel-aluminium bronze of the type CuAl10Fe5Ni5-C in a hydroelectric power plant. On turbine blades, the formation of green pustules composed of malachite with the chemical formula Cu2CO3(OH)2 was observed in river water under standing conditions.<br />NAB is a robust material widely used in marine applications with numerous literature related to its corrosion behaviour. However, no literature concerning fresh water applications could be found. The components in the power plant were constructed in a modular structure, constituting a contact element with a runner ring made of stainless steel.<br />Experimental results coincide with direct measurements in the power plant indicating that microbial ennoblement of the runner ring results in a rise of its potential relative to the runner made of NAB, sufficing observable progress in corrosion at the runner in moderate time frames (weeks).
en
dc.language
Deutsch
-
dc.language.iso
de
-
dc.rights.uri
http://rightsstatements.org/vocab/InC/1.0/
-
dc.subject
Korrosion
de
dc.subject
Nickel Aluminium Bronzen
de
dc.subject
Suesswasser
de
dc.subject
Süßwasser
de
dc.subject
MIC
de
dc.title
Korrosionsverhalten von Nickel-Aluminium-Bronzen in Süßwasser
de
dc.title.alternative
Corrosion-behaviour of nickel-aluminium bronzes in fresh water
en
dc.title.alternative
Korrosionsverhalten von Nickel Aluminium Bronzen in Süßwasser
en
dc.type
Thesis
en
dc.type
Hochschulschrift
de
dc.rights.license
In Copyright
en
dc.rights.license
Urheberrechtsschutz
de
dc.identifier.doi
10.34726/hss.2013.16310
-
dc.contributor.affiliation
TU Wien, Österreich
-
dc.rights.holder
Hans Philipp
-
tuw.version
vor
-
tuw.thesisinformation
Technische Universität Wien
-
tuw.publication.orgunit
E164 - Institut für Chemische Technologien und Analytik